| Thermal and Mechanical Properties of Polyvinyl Cloride | ||||||||||||
| Density= 1.4 g/cc | ||||||||||||
| T (K) | Thermal Expansion | Heat Capacity | Thermal Conductivity | Tensile Strength | Yield Strength | Young's Modulus | ||||||
| (%) | (J/gK) | (W/cmK) | (Psi) | (Psi) | (Psi) | |||||||
| 373 | 0.519 | |||||||||||
| 360 | 0.420 | |||||||||||
| 340 | 0.281 | |||||||||||
| 320 | 0.156 | |||||||||||
| 300 | 0.043 | 1.17E+00 | 4.093E-04 | 6.70E+03 | 5.15E+05 | |||||||
| 293 | 0.000 | 1.09E+00 | 3.900E-04 | 7.70E+03 | 5.20E+05 | |||||||
| 273 | -0.093 | 9.50E-01 | 3.550E-04 | 1.10E+04 | 5.25E+05 | |||||||
| 260 | -0.154 | 8.40E-01 | 3.300E-04 | 1.27E+04 | 5.30E+05 | |||||||
| 240 | -0.242 | 7.20E-01 | 2.950E-04 | 1.47E+04 | 5.35E+05 | |||||||
| 220 | -0.324 | 6.00E-01 | 2.700E-04 | 1.62E+04 | 5.40E+05 | |||||||
| 200 | -0.402 | 5.14E-01 | 2.416E-04 | 1.74E+04 | 5.50E+05 | |||||||
| 180 | -0.477 | 4.30E-01 | 2.200E-04 | 1.84E+04 | 5.80E+05 | |||||||
| 160 | -0.549 | 3.60E-01 | 2.000E-04 | 1.90E+04 | 6.20E+05 | |||||||
| 140 | -0.619 | 3.00E-01 | 1.850E-04 | 1.94E+04 | 7.10E+05 | |||||||
| 120 | -0.687 | 2.40E-01 | 1.750E-04 | 1.95E+04 | 8.20E+05 | |||||||
| 100 | -0.753 | 1.95E-01 | 1.680E-04 | 1.96E+04 | 9.50E+05 | |||||||
| 80 | -0.816 | 1.50E-01 | 1.97E+04 | 1.11E+06 | ||||||||
| 60 | -0.877 | 1.05E-01 | 1.98E+04 | |||||||||
| 40 | -0.934 | 6.47E-02 | ||||||||||
| 20 | -0.987 | 2.88E-02 | ||||||||||
| 10 | -1.010 | 9.33E-03 | ||||||||||
| 4.2 | -1.024 | |||||||||||
| T(K) = Temperature in Kelvin, T(C) = Temperature in Celsius | ||||||||||||
| T (C) = T (K) - 273 | ||||||||||||
| Thermal Expansion (%) = 100 x [L(T) - L(293)] / L(293) | ||||||||||||
| Heat Capacity [=] 1 J/gK = 0.23864 BTU/lbm/F | ||||||||||||
| Thermal Conductivity [=] 1 W/cmK = 57.77 BTU/hr/ft/F | ||||||||||||
| Tensile and Yield Strengths- lower bound values given | ||||||||||||
| Back to Property Main Page | ||||||||||||
| Do You Know Someone Who Needs A Job in Engineering, Physics or Chemistry? | ||||||||||||
| Note: The material of this page is copyrighted. No part of this page shall be copied, stored or reproduced without written permission. | ||||||||||||
| Disclaimer: The information of this page is provided to our best knowledge. However we are not responsible for any potential errors in the data. | ||||||||||||